ANYCUBIC ABS-lignende harpiks 3.0 (hvid)
ANYCUBIC ABS-lignende harpiks 3.0 (hvid) .
Betalingsmetoder
Betalingsmetoder
Vi tilbyder flere sikre betalingsmuligheder, så du nemt kan vælge den, der passer dig bedst:
✔ MobilePay – Betal hurtigt og sikkert med din mobil.
✔ Kreditkort – Vi accepterer VISA, Mastercard og Dankort.
✔ ViaBill – Køb nu, betal senere med fleksible afbetalingsmuligheder.
Levering eller afhentning
Levering eller afhentning
Bestil nemt – vælg levering eller afhentning i Vordingborg
Køb dit produkt hos os og vælg den leveringsmetode, der passer dig bedst:
🚚 Hurtig levering – Få din ordre leveret direkte til din adresse eller nærmeste pakkeshop. Vi samarbejder med pålidelige fragtfirmaer for sikker og hurtig levering.
📍 Lokal afhentning i Vordingborg – Ønsker du at spare fragttiden? Vælg lokal afhentning, og hent din ordre direkte hos os i Vordingborg. Vi sender en besked, så snart din vare er klar til afhentning.
Uanset om du vælger levering eller afhentning, sørger vi for en nem og problemfri shoppingoplevelse.
14 dages returret
14 dages returret
Klik her for hurtigt at bestille en returlabel
Nem og enkel retur inden for 14 dage
Vi ønsker, at du skal være tilfreds med dit køb. Hvis du fortryder dit køb, har du mulighed for at returnere din vare inden for 14 dage efter modtagelse.
For at varen kan returneres, skal den være i samme stand som ved modtagelsen – ubrugt, med eventuelle mærker påsat og i original emballage.
Kontakt os, hvis du ønsker at starte en returnering, så guider vi dig gennem processen. Vi gør det nemt og problemfrit for dig.
ANYCUBIC ABS-lignende harpiks 3.0 (hvid)
ANYCUBIC ABS-lignende harpiks 3.0 (hvid)
Betaling og Sikkerhed
Betalingmetoder
Dine betalingsoplysninger behandles sikkert. Vi gemmer ikke kreditkortoplysninger og har heller ikke adgang til dine kreditkortoplysninger.
Specifikationer
Specifikationer
ANYCUBIC ABS-Like Resin 3.0 (White)
ANYCUBIC ABS-Like Resin 3.0 is a photopolymer resin designed for LCD and DLP 3D printers, combining high mechanical strength, crack resistance, and high print accuracy. With an elongation at break of 25–30%, an impact strength of 130 J/m, and a low volumetric shrinkage rate (3.9–4.9%), it allows you to create durable models with a smooth surface and a very high level of detail. Low viscosity and minimal odor further enhance working comfort.
Greater flexibility and improved strength
ABS-Like Resin 3.0 is ideal for creating parts subjected to stress. With a hardness of 83–86 HD and high impact resistance, the finished models retain their durability even during drilling and further machining. The material also stands out for its very low susceptibility to warping, making it ideal for printing mechanical parts, device housings, and automotive components. Additionally, ABS-Like Resin 3.0 offers an elongation at break of up to 30%, which is nearly twice that of many standard ABS-type resins. These properties allow the material to better withstand stress and increase the models’ resistance to damage caused by everyday use.
High precision and shorter print times
Low shrinkage and an optimally selected viscosity of 280–300 mPa·s result in highly accurate detail reproduction and a smooth surface finish. The material’s good flow accelerates its return to the build volume, which helps reduce print time and increase productivity.
Comfort during printing and broad compatibility
The resin formula was developed to minimize odor and reduce the risk of irritation during use. You also don’t have to worry about compatibility issues—ABS-Like Resin 3.0 works with a wide range of LCD and DLP 3D printers that use UV light with a wavelength between 365 and 405 nm. This makes it ideal for both home workshops and more advanced projects.
| Manufacturer | ANYCUBIC |
|---|---|
| Model | ABS-Like 3.0 |
| Color | White |
| Material | Photopolymer resin |
| Wavelength | 365–405 nm |
| Viscosity | 280–300 mPa·s (25°C) |
| Density | 1.06–1.09 g/cm³ |
| Hardness | 83–86 HD |
| Tensile strength | 38–45 MPa |
| Elongation at break | 25–30% |
| Flexural modulus | 50–65 MPa |
| Flexural strength | 1500–2000 MPa |
| Young’s modulus | 1300–1700 MPa |
| Izod impact strength | 130 J/m |
| Volumetric shrinkage | 3.9–4.9% |
| Printing temperature | 20–50°C |
| Recommended ambient temperature during printing | 20–40°C |
| Exposure time for the first layer | 23–40 s |
| Exposure time for a standard layer | 2–3.6 s |
| Cleaning agent | 95% IPA |
| Washing time | ≥3 min |
| UV wavelength during curing | 405 nm |
| Curing temperature | 18–30°C |
| UV irradiance | 25,000–30,000 µW/cm² |
| Curing time | 3 min |
| Weight | 1 kg |